Nuclear Magnetic Resonance Investigation Of Dynamics In Poly(ethylene Oxide) Based Polyether-ester-sulfonate Ionomers

Open Access
- Author:
- Roach, David Jason
- Graduate Program:
- Chemistry
- Degree:
- Doctor of Philosophy
- Document Type:
- Dissertation
- Date of Defense:
- August 23, 2012
- Committee Members:
- Karl Todd Mueller, Dissertation Advisor/Co-Advisor
Tom Mallouk, Committee Member
Mary Beth Williams, Committee Member
Evangelos Manias, Committee Member
Ralph H Colby, Special Member - Keywords:
- NMR
Polymer Electrolytes
Single-ion Conductors
Ionomers
Polymer Dynamics
Cation Dynamics - Abstract:
- Nuclear magnetic resonance (NMR) spectroscopy has been utilized to investigate the dynamics of poly(ethylene oxide)-based lithium sulfonate ionomer samples that have low glass transition temperatures. 1H and 7Li spin-lattice relaxation times (T1) of the bulk polymer and lithium ions, respectively, were measured and analyzed in samples with a range of ion contents. The temperature dependence of T1 values along with the presence of minima in T1 as a function of temperature enabled correlation times and activation energies to be obtained for both the segmental motion of the polymer backbone and the hopping motion of lithium cations. Similar activation energies for motion of both the polymer and lithium ions in the samples with lower ion content indicate that the polymer segmental motion and lithium ion hopping motion are correlated in these samples, even though lithium hopping is about ten times slower than the segmental motion. A divergent trend is observed for correlation times and activation energies of the highest ion content sample with 100% lithium sulfonation due to the presence of ionic aggregation. Details of the polymer and cation dynamics on the nanosecond timescale are discussed and complement the findings of X-ray scattering and Quasi Elastic Neutron Scattering experiments. Polymer backbone dynamics of single ion conducting poly(ethylene oxide) (PEO)-based ionomer samples with low glass transition temperatures (Tg) have been investigated using solid-state nuclear magnetic resonance (NMR). Experiments detecting 13C with 1H decoupling under magic angle spinning (MAS) conditions identified the different components and relative mobilities of the polymer backbone of a suite of lithium- and sodium-containing ionomer samples with varying cation contents. Variable temperature (203-373 K) 1H-13C cross-polarization MAS (CP-MAS) experiments also provided qualitative assessment of the differences in the motions of the polymer backbone components as a function of cation content. Each of the main backbone components (PEO spacer and isophthalate groups) exhibit distinct motions, following the trends expected for motional characteristics based on earlier Quasi Elastic Neutron Scattering and 1H spin-lattice relaxation rate measurements. The temperature dependences of 13C linewidths were used to both qualitatively and quantitatively examine the effects of cation content on PEO mobility. Variable contact time 1H-13C CP-MAS experiments were used to further assess the motions of the polymer backbone on the microsecond timescale. The motion of the PEO spacer, determined from the rate of magnetization transfer from 1H to 13C nuclei, in all ionic samples becomes similar for T ≳ 1.1 Tg, indicating that the motions of the polymer backbones on the microsecond timescale become insensitive to ion interactions. These results compliment previous findings and present an improved picture of the dependence of backbone dynamics on cation type and density in these amorphous PEO-based ionomer systems. 7Li PFG NMR experiments provided measurements of the self-diffusion coefficients for Li+ cations in the PEO600-y Li ionomer series over a range of temperatures. When the Tg values are taken into account, the self-diffusion coefficients of Li+ in each sample follow a similar trendline, indicating that lithium diffusion is independent of ion concentration at any given reduced inverse temperature, Tg/T. Ion aggregation increases Tg and slows both lithium cation diffusion and displacement, but there is no further slowing beyond the Tg effect in the PEO600-y Li ionomers samples. The differences in activation energies obtained from diffusion measurements and relaxation times suggest that at least one additional barrier must be overcome for cations emerge from local hopping motion to macroscopic cation transport. Using the Nernst-Einstein equation lithium diffusion coefficients were also calculated from conductivity measurements. The differences between the diffusion measured by the two separate techniques indicate the presence of ion pairs. The activation energy of lithium diffusion was found to be nearly identical between the PFG NMR and conductivity, suggesting that the conductivity and ionic diffusion are related to the same ionic dynamics. As the ion content within the PEO600-y Li samples increases the relative concentration of non-conducting ion pairs decrease. Also an increase in temperature causes a fraction of ion pairs to thermally dissociate into positive triple ions.