IDENTIFICATION OF FUNDAMENTAL DEFORMATION AND FAILURE MECHANISMS IN ARMOR CERAMICS

Open Access
- Author:
- Muller, Andrea Marie
- Graduate Program:
- Materials Science and Engineering
- Degree:
- Doctor of Philosophy
- Document Type:
- Dissertation
- Date of Defense:
- July 29, 2011
- Committee Members:
- David John Green, Dissertation Advisor/Co-Advisor
David John Green, Committee Chair/Co-Chair
John Richard Hellmann Jr., Committee Member
Christopher L Muhlstein, Committee Member
Albert Eliot Segall, Committee Member - Keywords:
- Spherical Indentation
Ceramic Armor
Spinel
AlON
AlN - Abstract:
- Indentation of a surface with a hard sphere can be used to examine micromechanical response of a wide range of materials and has been shown to generate loading conditions resembling early stages of ballistic impact events. Cracking morphologies also show similarities, particularly with formation of cone cracks at the contact site. The approach in this thesis is to use this indentation technique to characterize contact damage and deformation processes in armor ceramics, as well as identify the role of cone cracking and inelastic behavior. To accomplish these objectives, an instrumented indentation system was designed and fabricated, extending depth-sensing capabilities originally developed for nano-indentation to higher forces. This system is also equipped with an acoustic emission system to detect onset of cone cracking and subsequent failure. Once calibrated and verified the system was used to evaluate elastic modulus and cone crack initiation forces of two commercial float glasses. As-received air and tin surfaces of soda-lime-silica and borosilicate float glass were tested to determine differences in elastic and fracture behavior. Information obtained from load–displacement curves and visual inspection of indentation sites were used to determine elastic modulus, and conditions for onset of cone cracking as a function of surface roughness. No difference in reduced modulus or cone cracking loads on as-received air and tin surfaces were observed. Abraded surfaces showed the tin surface to be slightly more resistant to cone cracking. A study focusing on the transition from elastic to inelastic deformation in two transparent fine-grained polycrystalline spinels with different grain sizes was then conducted. Congruent experiments included observations on evolution of damage, examinations of sub-surface damage and inspection of remnant surface profiles. Indentation stress–strain behavior obtained from load–displacement curves revealed a small difference in yielding and strain-hardening behavior given the significant grain size difference. Directly below the indentation sites, regions of grain boundary cracking, associated with the inelastic zone, were identified in both spinels. Comparison of Meyer hardness and in-situ hardness showed a discrepancy at low loads, a result of elastic recovery. Elastic-plastic indentation behavior of the two spinels was then compared to behavior of a transparent large-grained aluminum oxinitirde (AlON) and a small-grained sintered aluminum nitride (AlN). Subsurface indentation damage revealed transitions from intergranular to transgranular fracture in the two spinels, AlON showed a transition from multiple cleavage microcracks to transgranular fracture while AlN exhibited only intergranular fracture. Analysis of indentation stress-strain results showed a slight difference in yielding behaviors of the two spinels and AlON whereas AlN showed a much lower yield value comparatively. Slight differences in strain-hardening behavior were observed. When comparing indentation stress–strain energy density and work of indentation a linear correlation was observed and a clear distinction could be made between materials. Therefore, it is suggested by the work in this thesis that instrumented spherical indentation could serve as a useful method of evaluating armor materials, particularly when behavior is described using indentation stress and strain, as this is a useful way to evaluate onset and development of inelastic deformation under high contact pressures and self-confining stresses. Additionally, it proposes that comparison of the work of indentation and indentation strain energy density approaches provide a good foundation for evaluating and comparing a materials penetration resistance.